Notes of the high and low temperature alternating humidity temperature test chamber

1.When the cabinets temperature≥55℃,please don’t open the refrigeration compressor  in order to ensure normal operation of the compressor long life.

2.When the cooling function of the product to handing,the inclination shall not exceed 45℃ after in place，you should put 1_2 days and then boot,it is make for normal operation and prolong life of the refrigeration system.

3.In order to ensure the safety of  equipment and testing,please install an external protective earthing, according to the requirement to supply power.

4. High and low temperature alternating temperature humidity test chamber prohibited test of the flammable ,explosive,poisonous, and highly corrosive product.

5. Non-professionals may not disassemble, repair.

6. The device should be grounded.

7.High and low temperature alternating temperature humidity test chamber have not explosive devices,please don’t put on the inflammable , explosive and drying items.

8.When you operate testing,please don’t open the cabinet door, it may cause personal injury and equipment malfunction.

9.The door lock can only be opened from the outside, if you want to into the tank must be someone guardianship.

10.If the chamber into the heating sample,the sample is using external power,please don’t  directly use equipment itself power.

11.The apparatus is provided with a variety of protective measures, please regularly check.

12.Never gravity opening / closing door products, otherwise easily lead to the door fall off, causing damage to the product, resulting in injury.

13.When to stop using the product for a long time, should regularly do get rid of the moisture treatment, to avoid damage on the device.

14.When you carry high and low temperature test chamber , should be careful to avoid panel the instruments such as consumable. 

Colorimeter is analyze theory

Colorimeter for color control process to detect the color can be divided into two parts, one is the color detection, and the other part is the color analysis. Whether detection or analysis is required very high, only two step_outs are handled properly measured color information is the most authentic and reliable.

Measurement is determined chromatic meter internal result, analysis is the international and national standards. In 1931 the National Commission on Illumination (CIE)for the analysis of colorimeter establish a series of color space standard of the visible spectrum . Basically for colorimeter analysis provides a theory standard and basis, CIE color space standard is CIE_XYZ, the establishment of this color space is the basis for standards_based visual ability of the observer to realize, that he responded to the standard people eye visible range of colors. In addition CIE_XYZ, CIE_xyY, CIE_Lab, CIE_Lch other standard color space, suitable for different industries and products.

Currently colorimeter is commonly used built_in color space CIE Lab color space, the color space to represent the color of the lightness L value, a value represents the value of the color red and green, b value represents the value of the color blue and yellow.

CIE Lab is mainly defined of really product color different value, generally used for all types of colorimeter color to control change. Lab values of a single set of little practical significance, but can only through the Lab when compares two color difference value to judge the difference between them.Precision colorimeter can measure the Lab values of the object obtained by analyzing the difference between the two colors. Lab value through long_term observation of the results we find that when the difference between Lab values greater than 1:00 naked eye can clearly feel the presence of chromatic aberration. Now the industry to save time and improve productivity, are generally used a pre_set tolerance range, during the quality control sample measured as long as the tolerance range on qualified, whether the person is ineligible. So not only can control the color quality of the products while increasing efficiency. By using the Lab color space, our production control to achieve the data.

Factors of the affecting gloss paint

It mainly depends on the illuminating source and angle of observation, the instruments measurement is adopt  20 °, 60 °, 85 ° angle of illumination and detection signal. Different industries often use different angle measuring instruments.

Surface gloss measurement ink, paint, baked enamel , coating, wood products surface gloss measurement; architectural decoration materials, marble, granite, vitrified tiles, ceramic tiles and other surface gloss measurement; plastic, paper and other surface gloss measurement; Other non-metallic surface gloss measurement.

Factors of the affecting gloss finish paint:

1)the deployment of paint, increasing the amount of curing agent, the gloss will rise;

2) If reducing the amount of curing agent, the gloss is reduced;

3) increasing the amount of thinner, paint good leveling, thin brush can be, gloss reduction;

4) reduce the amount of thinner, paint leveling poor, must be thick brush, gloss increased; 

5) coating thickness, high gloss; thin coating, low gloss. Whether high or low gloss substrates,Brush paint dumb smooth is matte effects, brush light finish is too light effects.

 Secondly, the luster has relation with the pigments and fillers . Pigment particle size is large, usually someextinction. Particle size is too small, high oil absorption of paint, but also has a certain luster affected. Some people talked about the impact of filler above, substantially all of the filler material will affect the gloss, but I have seen ultrafine barium sulfate , does not substantially affect on the gloss, may even increase the gloss in thecase of an appropriate amount to add.

 Last, the impact of the dispersant influence is very large. If it is paint, must take into account the impact of the dispersant. Done related tests, the same formula, using different dispersants, a glossy 80 Another over 40. This is because the use of inappropriate dispersant, pigment will flocculation, the particles will be coarse, affect the gloss is inevitable.

 

Rockwell hardness tester are advantages and disadvantages

Rockwell hardness tester advantages are:

1. because Rockwell hardness tester have a hard and two soft head, it is adapted to test a variety of different hard materials, there is no pressure head deformation;

2. small indentation, not to hurt the surface;

3. rapid operation, immediately obtained data, high production efficiency, suitable for mass production of the finished product testing.

 Rockwell hardness tester disadvantages are:

With different hardness level measured hardness value cannot unify ,can not be compared. Rockwell hardness value on the provisions of the production in the most used is A-class, B-class and C-class, namely the HRA, HRB and HRC, and among which the most commonly HRC. Because Rockwell hardness tester is the indentation depth t pouch as an index measure hardness values. At the same hardness level, the more hard metal indentation depth t is smaller, the more flexible the t greater. If directly with the size of the t as indicators, there will be a small hard metal t value and hardness values, the t value of soft metal hardness value is big to the phenomenon of large, this and brinell hardness value represented by the hardness of the concept of size, also do not match the habits of people. For this reason, only a last resort to take measures, namely with the selected constant minus the t values to mark its difference Rockwell hardness values. This constant provision of 0.2mm and 0.26mm. Rockwell hardness of the indenter divided in two soft and hard. Hard by the apex angle of 120 ° diamond cone into the system, suitable for measuring harder hardening steel and other metal materials; soft diameter 1/16 "or 1/8" steel ball, suitable for annealing Determination of steel, nonferrous metals and other softer material hardness values. Rockwell hardness of the applied load is tested according to hard and soft metal itself differently ranging provisions with different indenter and the applied loads with different titles appeared in a variety of Rockwell hardness level.